SCREW DESIGN OF LOW MFI PE/PP MATERIAL, Blow Molding (Machine)

Kenplas Forum ==> Blow Molding (Machine) ==> SCREW DESIGN OF LOW MFI PE/PP MATERIAL

SIR,
CAN ANY ONE SUGGEST A RIGHT DESIGN OF SCREW FOR SOLUTION OF OUR PROBLEM?

WE PROCESS 0.30 MFI HDPE MATERIAL TO MAKE PE PREFORMS (WHICH IS BLOWN INSINGLE STAGE IBM M/c) WT. RANGING 60g ~ 100g ON A IBM M/c HAVING 45 Dia. SCREW & 160 + 10 mm STROKE.

WE R FACING A PROBLEM OF GENERATING OF BLACK & BROWN SPECS RANDOMLY AFTER FEW WEEKS.

ON INCREASING A COMPRESSION RATIO FROM 1.35 TO 1.6, IT WAAS REDUCED TO 40% BUT ANOTHER QUALITY RELATED PROBLEMS LIKE BLACK LINE ALONG P[ARTING LINE HAS BEEN STARTED.

2009-12-28 15:15:14 By sanjay mehta


*Post A Reply*
	Temporarily shut down, no new message, sorry.
Name:	..Invalid Name..
Email:	..Invalid Email.. Send new posts of this topic to my email box.
Message:	(Max. 2KB)
Message:	..Invalid Message..
Attachment:	(Max. 500kB, .RAR.ZIP.JPG.GIF only)
Verification:	..Invalid Code..

This forum published since July 03, 2002. Renewed on June 22, 2005.

[Plastics Project]	[Plastics Machinery]	[Plastics Mold]	[Discussion Forum]	[Contact Kenplas]
Copyright © 2024 Kenplas Industry Limited, Hangzhou Kenplas Machinery Ltd. Powered by Alentus.